The SPE Library contains thousands of papers, presentations, journal briefs and recorded webinars from the best minds in the Plastics Industry. Spanning almost two decades, this collection of published research and development work in polymer science and plastics technology is a wealth of knowledge and information for anyone involved in plastics.
The SPE Library is just one of the great benefits of being an SPE member! Are you taking advantage of all of your SPE Benefits?
Jie Chen, Lih-sheng Turng, Tao Liu, Ling Zhao, Wei-kang Yuan, May 2013
This work aimed to investigate the crystallization behavior of microcellular injection molded polypropylene (PP)/nano calcium carbonate (nano-CaCO3) composites. The effects of processing conditions, such as injection speed, mold temperature, and CO2 concentration as well as the filler concentration, on the crystal form, crystal orientation, and crystallinity were studied using 2D-wide-angle X-ray diffractometer (2D-WXRD) and differential scanning calorimeter (DSC). The ?-form crystal was found in the surface layer of injection molded samples under high injection and mold temperature, due to the high shear stress. The addition of nano-CaCO3 filler promoted the formation of ?-form crystal while the foaming process inhabited its formation. The orientation degree calculated from XRD images by Hermans function showed a high value in the surface layer and it decreased as the distance from the surface increases. Meanwhile, the orientation degree reduced with foaming and the addition of filler, as both the bubbles and fillers disturbed the orientation of molecular chains. The degree of crystallinity of samples was higher in the surface layer and increased with foaming. However, the degree of crystallinity reduced with the addition of fillers and showed no dependence on injection speed and mold temperature.
Xiaoqing Fan, Feng Chen, Jintao Yang, Mingqiang Zhong, May 2013
Polyamide 46 (PA 46)/graphene oxide (GO) nanocomposites were successfully prepared using a solution mixing technique. Differential scanning calorimetry results illustrated that adding a small amount GO facilitated the nucleation of PA 46. Avrami analysis showed a decrease in the dimension of PA 46 crystal growth in the composites because of a constrained environment formation. The equilibrium melting temperature (Tm) of PA 46 increased in the composites,. Laser flash analysis exhibited that thermal conductivity of nanocomposites increased 50 % compared with neat PA 46. The thermal stability of nanocomposites was also improved.
Two surface modifiers, phenyl isocyanate, and poly(ethylene glycol) (PEG800), which have different affinities to the hard and soft segments in polyurea, were used to synthesize functionalized graphene oxides (GO). After the modification, the PEG800-modified (PEG800-GO) and phenyl isocyanate-modified (i-GO) GOs were highly exfoliated and dispersed in DMF. Using the suspension of the functionalized GO,. Polyurea/GO composites were prepared using a solution-blending method.It was shown that PEG800- GO and i-GO are uniformly dispersed throughout the polymer matrix on a nanoscale. The well-dispersed GO platelets improved the thermal stability and mechanical properties of polyurea. PEG800-GO, which has a strong affinity for the soft segments, shows a more significant reinforcing effect. At 2.0 wt% GO, the tensile strength of polyurea was enhanced by ~75%.
Yuejun Liu, Xiumei Pan, Yiwu Liu, Lih-Sheng Turng, May 2013
High-density polyethylene (HDPE)/nano-SiO2 and polypropylene (PP)/nano-SiO2 films have been prepared by two different processing conditions; i.e., under traditional steady state (TSS) conditions and with a vibration force field (VFF). The aim of this research is to study the crystallization and barrier properties of films manufactured under different processing conditions. The results showed that the barrier and mechanical properties of the nanocomposites processed under the VFF condition were superior to those processed under the TSS condition. Differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) were used to characterize the crystalline structure and morphology of the films, which provided evidence for explaining the distinct barrier and mechanical properties under the two processing conditions. DSC and SEM results clearly showed that an increase in the degree of crystallinity and orientation of the lamella were found in the nanocomposites prepared under the VFF condition.
Shaun Eshraghi, Mehdi Karevan, Suman Das, Kyriaki Kalaitzidou, May 2013
This research focuses on manufacturing multifunctional polymer nanocomposites (PNCs) using selective laser sintering (SLS). Carbon-based nanofillers such as carbon fibers, carbon nanotubes, carbon black, and graphene can be used to induce thermal and electrical conductivity in polymers, enabling them for a wide range of applications that require lightweight multifunctional materials. In this study, the SLS processing of PNCs of polyamide-12 (PA) with graphene nanoplatelets (GNP) at 3 and 5 wt% is optimized to achieve PNCs that are nearly fully dense and exhibit homogeneous dispersion and distribution of the platelets. Observation of the filler-coated polymer’s microstructure after compounding and SLS processing shows the most homogeneous dispersion of nanofiller with GNP at 3 wt%. At 3 wt% the highest tensile modulus (2.1GPa) is also achieved. The part density of the optimally SLS-processed neat PA and PNCs are all nearly fully dense (>96%) and the highest density (99.5%) is again found at 3 wt% GNP.
The usefulness of thermoplastic injection-molding simulation is influenced by many simulation inputs – such as the modeling of part geometry, mesh type and density, mathematical solution, process settings, and plastic material properties both as melt and as solid. Since 2008, much progress has been made with regards to meshing capability and to having robust solution algorithms, but the material properties data file still remains as a weak link in the simulation process. This paper reviews the results of a validation study that focused on the influence of the material properties data file on the precision and accuracy of Moldflow 2012.
Nisa V. Salim, Nishar Hameed, Tracey L. Hanley, May 2013
The self-assembly of ABC triblock copolymer/homopolymer blends where the homopolymer is miscible with one of the blocks (C) and immiscible with the other two blocks (A and B) of the block copolymer were investigated. The well-known proton donating polymers, -namely, phenoxy and poly (4-vinyl phenol) (PVPh) were used to prepare the self-assembled SBM triblock copolymer blends. In these blends, microphase separation takes place due to the disparity in intermolecular interactions; specifically, the homopolymer interacts with PMMA blocks through hydrogen bonding interactions. In both PVPh/SBM and phenoxy/SBM blends, order to disorder morphology transitions were observed with increase in homopolymer content. The TEM and SAXS results of phenoxy/SBM show lamellar, bicontinuous and other disordered nanostructures; whereas in PVPh/SBM, lamellae, hexagonal close packed cylinders, and other complex disordered nanostructures were observed. Here we examined how intermolecular hydrogen bonding interaction between the homopolymer and block copolymer can alter the morphologies of the blends.
Siu Ning (Sunny) Leung, Ellen Chan, Hani Naguib, Francis Dawson, May 2013
This paper examines polyphenylene sulfide (PPS)-based composite materials filled with different types of hexagonal boron nitride (hBN) particulates. It aims to investigate the effect of filler geometry on the multifunctional properties of the polymer-matrix composites (PMCs). Experimental results revealed that the PPS-hBN composite filled with hBN platelets of varying particulate sizes and shapes led to the largest improvement in the PMC’s effective thermal conductivity. It also led to the greatest reduction in the PMC’s coefficient of thermal expansion. In addition, the electrical of the PPS-hBN composites were studied. It was found that the addition of hBN did not compromise the electrical resistivity of neat PPS. In terms of PPS-hBN mechanical properties, the PMCs’ compressive moduli were promoted while their compressive strengths were suppressed. In short, the size and shape of hBN particulates would influence the thermal, electrical, and mechanical properties of the PPS-hBN composites.
An isotactic polypropylene-polydimethylsiloxane (iPP-PDMS) elastomer was prepared by reactive extrusion with tert-butyl peroxide. Rheology and thermomechanical analyzer (TMA) experiments demonstrate typical elastomeric behavior. Two complimentary techniques TMA and differential scanning calorimetry (DSC) were combined to estimate the density of iPP in the crystalline phase and to calculate the volume change associated with melting and crystallization thermal transitions. Further, the analysis confirmed the presence of crystalline iPP and amorphous PDMS phases in the elastomer
Jihun An, Byoung-Ho Choi, Chulhong Kim, Jeong-Moo Lee, May 2013
For the commercial production of consumer products using engineering polymers, it is very important to control physical properties of the material. However, due to many reasons, e.g. cost reduction, cleaning issues, using scraps etc., the quality control of the material is not easy. In many cases, the effect of a small amount of foreign polymers on product failures is well known, but it is difficult to analyze them by conventional analytical techniques. So, in this paper, the methodology of evaluating the durability of Acrylonitrile Butadiene Styrene (ABS) copolymer containing foreign polymers using fracture mechanism maps is introduced. In addition, as a quantitative tool, the importance of the ductile-to-brittle transition temperature (DBTT) is discussed.
Joonsung Tae, Janghwan Kim, Jinsu Gim, Hyungpil Park, Byungohk Rhee, May 2013
In order to keep the part quality under a stable mold temperature, a number of parts should be discarded until the mold temperature reaches to a stable condition. Depending upon process and environmental conditions, the time to a stable condition varies. In this work, influencing factors to the stabilized mold temperature condition are examined. The results show that ambient temperature significantly affects the stabilization time. To predict the stabilization time with consideration of heat transfer to the molding machine, heat sink attached model in the CAE analysis was suggested. It shows a good agreement with experimental result.
Zhiliang Fan, Huagang Yu, Jiping Xu, Jiping Xu, May 2013
Buckling analysis is useful for identifying if thin-walled polymer injection molded parts buckle due to in- mold residual stresses after ejection. However, traditional direct-solver-based eigen-solvers become prohibitively expensive for large-scale three-dimensional (3D) finite element models for injection molding simulation. A new fast parallel eigen-solver has been developed, which combines an algebraic multigrid preconditioned conjugate gradient (AMG-CG) equation solver with a subspace eigenvalue iteration algorithm, making the large-scale 3D buckling analysis feasible for industrial applications. The buckling analysis has been extended to the injection over-molding process. Buckling analysis results for a simple tray model and an insert over-molded part are presented.
In injection molding process, the fluid-structure interaction (FSI) issue has been widely discussed, especially for core shift deflection problem recently. During the filling stage, a non-uniform pressure distribution within the cavity leads to common structural deformation defects. At the same time, the deformed structure affects filling behaviors. These dynamic deformations and fluid mechanics result in the difficulties of maintaining numerical simulation accuracy and huge computational memory.
In this paper, a new iterative FSI coupling method has been developed. The new method not only provides more accurate melt front and pressure result but also predict precisely core deflection simultaneously. Furthermore, a new solid mesh deformation technique is used to rebuild cavity solid mesh automatically in accordance with continually deformed cavity geometry. Moreover, a real case is applied for both numerical simulation and experimental study to validate the iterative FSI coupling method. The results in this paper demonstrate that the high quality deformed meshes are reliable and help to get a good agreement with experiment.
Yuqiu Yang, Kosuke Togashi, Mengyuan Liao, Hiroyuki Hamada, May 2013
In this paper, the effects of fiber surface treatment on the mechanical and thermal properties of glass woven fabric reinforced thermosetting epoxy resin matrix composites are examined experimentally. Four kinds of deposit (pick-up) ratios of polyurethane dispersion (PUD) treatments on the heat-cleaning glass cloth woven fabric were carried out, including 0wt% (without treatment), 0.76wt%, 1.51wt% and 6.49wt%. It is found that the interfacial adhesion and property were affected by the treatment significantly. The correlation among varied PUD surface treatment pick-up ratio of glass fiber, modified interface, improved mechanical property and related thermal property were discussed and clarified based on tensile test, dynamic mechanical analysis (DMA), scanning electronic microscope (SEM) observation.
Supercritical carbon dioxide (scCO2) was used in extrusion for the improvement of polymer blend properties. The compounding took place in two-single screw extruder. The morphologies of prepared blends were compared. Carbon dioxide was added at 3, 5wt% based on polymer melt flow rates. The experimental results indicate that the viscosity of PP and PS blends were reduced obviously and a sharp decrease in the size of the dispersed phase was observed. The impact strength of press molded 80/20 polypropylene /polystyrene blends increase by the addition of CO2.
Guifang Shan, Ting Zhou, Minghua Luo, Minqi Xin, May 2013
The effect of the blending sequence and the viscosity ratio on the phase morphology and mechanical properties of blends of polypropylene and polyphenylene ether was investigated in present study. It is found that that the Izod impact strength of PPE/PP alloy compounded via two step extrusion method can be improved significantly. A preblending SEBS with PPE can make the compatibilizer SEBS move easily to the PPE/PP interface and the blends had finer dispersion and better properties. Also, the experimental results have showed a clear dependence of the blend phase morphology and properties on the viscosity ratio. The Izod impact strength of PPE/PP blend can be improved by decreaseing the viscosity ratio ?PPE/?PP. In addition, the screw configuration containing an elongational flow field has proved to be more effective in deforming particles than a shear flow field, leading to finer dispersion and better properties.
Ping Fan, Fanlin Huang, Hanxi Zhang, Jie Feng, MIngqiang Zhong, May 2013
Graphene oxide/PNIPA ?GO/PNIPA ?composite were successfully prepared through in-situ polymerization. And then using chemical reducing agent, GO/PNIPA was reduction tographene/PNIPA composite. Resulting hydrogels were characterized by FTIR, scanning electron microscopyto investigate the structural, morphologicalproperties. The swelling ratio and response kinetics on heating or cooling were also investigated to understand the smart properties. The result indicated that graphene/PNIPA hydrogel showed good smart property with a higher swelling ratio and more complicated deswelling behavior.
Shahid Ahmed, Jamal AlSadi, Usman Saeed, Ghaus Rizvi, Daniel Ross, May 2013
Historical colour data of a compounded plastic grade manufactured at Sabic IP Cobourg Plant has been analysed through statistical means. Objective was to investigate response of output colour to small adjustments in pigments standard formulation recommended to impart desired colour to a plastic grade. The Plastic grade studied was a blend of two polycarbonate resins, five additives and four colour pigments including one organic – the black pigment, and three inorganic - white, red and yellow pigments. Color mismatch caused by these adjustments is presented in terms of dL*, da* and db*. Analysis of colour deviation caused by such adjustments reveals that output colour values are more sensitive to perturbations in white and yellow pigments amount compared with black and red. Results of optimization carried out to minimize colour deviation, are also presented for the plastic grade.
Shahid Ahmed, Jamal AlSadi, Usman Saeed, Ghaus Rizvi, Daniel Ross, Richard Clarke, James Price, May 2013
For plastic compounders it is imperative to acquire a profound understanding of relationship between extrusion process variables and compounded plastics colour for achieving consistency in output colour. Compounders also need to take educated and precise decisions while incorporating any changes in process variables to minimize deviation of output response from target colour for a compounded plastic. Such a relationship has been investigated using an efficient and economic design of experiments (DOE) for a polycarbonate resin-based compounded plastic. Present study has discussed the results of designed experiments and shed an insight on individual as well as combined influence that process parameters impose on output colour. Three process parameters under study are temperature, feed rate and screw speed. Results of confirmation DOE has also been discussed, which have verified fitness of statistical model used for analysis. The study further suggests a set of optimal process conditions that could be implemented ensuring consistency in compounded plastic colour with minimum deviation from target.
Robert Romano, Smruti Patil, Daniel F. Schmidt, May 2013
Bisphenol A is a key component of many epoxy resins, but is under pressure especially in food contact applications, necessitating the identification of high performance alternatives. In this work we report on the preparation, properties and performance of one such alternative, the bis(epoxide) of 2,2,4,4-tetramethyl-1,3-cyclobutanediol. This resin has been crosslinked with a typical amine hardener to produce a stiff, hard thermoset with a high Tg. Curing behavior and cured resin properties are improved vs. the bis(epoxide) of cyclohexanedimethanol, a structural isomer of CBDO. Compared to a BPAbased equivalent, resin viscosity and UV cutoff are lower and lap shear adhesion to mild steel is superior, the latter on par with a commercial heavy duty epoxy adhesive. These results indicate promise from this material as a high-performance BPA-free epoxy resin.
84 countries and 60k+ stakeholders strong, SPE
unites
plastics professionals worldwide – helping them succeed and strengthening their skills
through
networking, events, training, and knowledge sharing.
No matter where you work in the plastics industry
value
chain-whether you're a scientist, engineer, technical personnel or a senior executive-nor
what your
background is, education, gender, culture or age-we are here to serve you.
Our members needs are our passion. We work hard so
that we
can ensure that everyone has the tools necessary to meet her or his personal & professional
goals.
Any article that is cited in another manuscript or other work is required to use the correct reference style. Below is an example of the reference style for SPE articles:
Brown, H. L. and Jones, D. H. 2016, May.
"Insert title of paper here in quotes,"
ANTEC 2016 - Indianapolis, Indiana, USA May 23-25, 2016. [On-line].
Society of Plastics Engineers
Available: www.4spe.org.
Note: if there are more than three authors you may use the first author's name and et al. EG Brown, H. L. et al.
This site uses cookies to recognize members so as to provide the benefits of membership. We may also use cookies to understand in general how people use and visit this site. Please indicate your acceptance to the right. Learn More..